Abstract
A comb-like acrylamide copolymer (HCJ-1) was synthesized by using aqueous free radical polymerization of acrylamide (AM) as main monomer and ether carboxylate as functional monomer. The copolymers were characterized with FT-IR and SEM. The SEM results show that the molecular structure of copolymer is extended in salt water. It is proved that the copolymer shows good salt resistance.The solution properties of HCJ-1 were studied and compared with those of partially hydrolyzed polyacrylamide (HPAM). The experimental results show that the obtained HCJ-1, compared with HPAM, exhibits a dramatic enhancement in the salt-resistant properties. The apparent viscosity retention rate of 1.5 g L HCJ-1 aqueous solution and salt solution after 180 days at 60 °C are 70.6% and 64.5%, respectively, exhibiting good thermal stability. In addition, HCJ-1 solution also displays the excellent shearing resistance. In a word, the experimental results show the HCJ-1 is a promising profiling agent for high salinity reservoir.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.