Abstract
Natural vermiculite was modified by cation exchange with long-chain quaternary alkylammonium salts and then dispersed in polyether-based polyols with different structures and ethylene oxide/propylene oxide ratios. The dispersions were evaluated by X-ray scattering and rheology. In all polyol dispersions tested, polyols were intercalated into the vermiculite interlayers. Also, significant shear thinning behavior was observed. A large interlayer spacing of ∼90 Å was achieved in one polyol suitable for polyurethane elastomer synthesis. In polyurethane made with this polyol, clay platelets were extensively intercalated or exfoliated. The composites showed a >270% increase in tensile modulus, >60% increase in tensile strength, and a 30% reduction in N(2) permeability with a loading of 5.3 wt % clay in polyurethane. Differential scanning calorimetry and dynamic mechanical analysis revealed that the nanoclay interacts with the polyurethane hard segments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.