Abstract
AbstractPhosphate cancrinite (PO4‐CAN) has been synthesized under mild hydrothermal conditions at 473 K using kaolin, sodium orthophosphate‐dodecahydrate and strong alkaline conditions (8 M NaOH solution). Cancrinite crystals of rod‐like habit and maximum lengths up to 2 μm were observed and characterized by X‐ray powder diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X‐ray spectroscopy (EDXS) and Fourier transform infrared spectroscopy (FTIR). Magic angle spinning nuclear magnetic resonance spectroscopy (MAS NMR) of the nucleus 31P, thermogravimetry (TG/DTG) and heating experiments under open conditions in a furnace were additionally performed. The empirical formula Na8[SiAlO4]6(PO4)0.58(CO3)0.13(H2O)4.6 was calculated from EDXS analyses and TG data under consideration of a minor carbonate content, detected by FTIR spectroscopy. PO4‐CAN is stable up to 800 °C before thermal destruction rapidly occurs at 825 °C. The final product of TG analyses at 1000 °C is a mixture of a nepheline‐like phase and the phosphate content of the initial cancrinite sample. XRD and FTIR results of the synthesis product are in good agreement with literature data of the rare mineral depmeierite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Zeitschrift für anorganische und allgemeine Chemie
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.