Abstract
Epitaxial ZnO thin films doped uniformly with nitrogen at 1020 atoms/cm3 were fabricated by pulsed laser ablation of a Zn-rich Zn3N2 target. The films grown at 300 °C and annealed at 600 °C in O2 showed p-type conductivity. Two acceptor levels at 105 and 224 meV were determined by temperature-dependent Hall and photoluminescence measurements of the p-type samples. Transmission electron microscopy studies revealed that the p-type ZnO films consist of 10–20 nm columnar grains with a high density of defects and grain boundaries that may facilitate the annihilation of native donors and the activation of acceptors during postdeposition annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.