Abstract
Biodegradable polyurethane was synthesized using poly(DL-lactic acid) diol and hydroxytelechelic natural rubber as hydroxyl containing precursor, 1,4-butane diol as chain extender, isophorone diisocyanate and dibutyltin dilaurate as catalyst. Poly(DL-lactic acid) diol was prepared by condensation polymerization of DL-lactic acid using 1,4-butane diol as initiator and stannous octoate as catalyst. Hydroxyltelechelic natural rubber synthesized via oxidative degradation of natural rubber and then reduced carbonyl end group to hydroxyl group. Chemical structure of products was characterized by 1H-NMR. Molecular weight and polydispersity determined by SEC. Thermal properties was characterized by DSC and TGA. Segmented polyurethane show two Tgs and two degradation steps corresponding to natural rubber and poly(DL-lactic acid) segment. Polyurethane containing poly(lactic acid) more than 40%mol are become brittle. This result caused by brittle characteristic of PLA. Moreover, mechanical properties increased as content of PLA increased.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.