Synthesis and properties of new aromatic polyimides based on 2,5‐bis(4‐amino‐2‐trifluoromethylphenoxy)‐tert‐butylbenzene and various aromatic dianhydrides

Abstract

AbstractA novel, fluorinated diamine monomer, 2,5‐bis(4‐amino‐2‐ trifluoromethylphenoxy)‐tert‐butylbenzene (II) was synthesized through the nucleophilic substitution reaction of tert‐butylhydroquinone (t‐BHQ) and 2‐chloro‐5‐nitrobenzotrifluoride in the presence of potassium carbonate to yield the intermediate dinitro compound I, followed by catalytic reduction with hydrazine and Pd/C to afford diamine II. A series of fluorinated polyimides V were prepared from II with various aromatic dianhydrides (IIIa–f) via the thermal imidization of poly(amic acid). Most of Va–f could be soluble in amide‐type solvents and even in less polar solvents. These polyimide films showed tensile strengths up to 106 MPa, elongation at break up to 21%, and initial modulus up to 2.1 GPa. The glass‐transition temperature of V was recorded at 245–304 °C, the 10% weight loss temperatures were above 488 °C, and left more than 41% residue even at 800 °C in nitrogen. Low dielectric constants, low moisture absorptions, and higher and light‐colored transmittances were also observed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5424–5438, 2004