Synthesis and properties of fluorinated biphenyl‐type epoxy resin

Abstract

AbstractA novel fluorinated biphenyl‐type epoxy resin (FBE) was synthesized by epoxidation of a fluorinated biphenyl‐type phenolic resin, which was prepared by the condensation of 3‐trifluoromethylphenol and 4,4′‐bismethoxymethylbiphenyl catalyzed in the presence of strong Lewis acid. Resin blends mixed by FBE with phenolic resin as curing agent showed low melt viscosity (1.3–2.5 Pa s) at 120–122°C. Experimental results indicated that the cured fluorinated epoxy resins possess good thermal stability with 5% weight loss under 409–415°C, high glass‐transition temperature of 139–151°C (determined by dynamic mechanical analysis), and outstanding mechanical properties with flexural strength of 117–121 MPa as well as tensile strength of 71–72 MPa. The thermally cured fluorinated biphenyl‐type epoxy resin also showed good electrical insulation properties with volume resistivity of 0.5–0.8 × 1017 Ω cm and surface resistivity of 0.8–4.6 × 1016 Ω. The measured dielectric constants at 1 MHz were in the range of 3.8–4.1 and the measured dielectric dissipation factors (tan δ) were in the range of 3.6–3.8 × 10−3. It was found that the fluorinated epoxy resins have improved dielectric properties, lower moisture adsorption, as well as better flame‐retardant properties compared with the corresponding commercial biphenyl‐type epoxy resins. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009