Abstract
Oxynitride phosphors M0.98Si2O2N2: Eu0.022+ (M=Ba, Sr, Ca) for white LEDs were synthesized at 1300, 1400, and 1500°C by using the partially cellulose assisted liquid phase precursor (PLPP) process and compared with solid state reaction (SSR) process. MSi2O2N2 (M=Ba, Sr, Ca) crystal structure was obtained from M0.98Si2O2N2: Eu0.022+ phosphor fired at 1400°C using the PLPP process. However these phosphors were not synthesized through the SSR process at same temperature. M0.98Si2O2N2: Eu0.022+ (M=Ba, Sr, Ca) phosphors from PLPP produced a blue color emission at 487nm (380nm excitation), a green color emission at 528nm (374nm excitation), and a yellow color emission at 538nm (371nm excitation). M0.98Si2O2N2: Eu0.022+ phosphors from PLPP had higher luminescence and crystallinity compared with those obtained from the SSR process. The prepared phosphors were analyzed by X-ray diffraction (XRD), photoluminescence (PL) and field-emission scanning electron microscopy (FE-SEM).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.