Abstract
Abstract Hollow Microspheres of SiO 2 -TiO 2 photocatalysts whose walls are made up of mesoporous cellular foams were synthesized with the aid of hexane as a swelling agent and P123 as a pore template by an emulsion templating method. Pore structure of materials and crystal phase of titanium oxide was tailored by hydrothermal and calcination temperature during synthesis of samples. The samples were characterized with field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), N 2 adsorption–desorption experiments, X-ray photoelectron spectroscopy (XPS) and X ray diffraction (XRD) techniques. The effect of pore structure and titania phase on photoactivity were evaluated by methylene blue (MB) degradation test under UV light as well. Results showed that hydrothermal temperature during synthesis process has a significant effect on pore and window sizes of mesostructured cellular foam. Interestingly, for the sample hydrothermally treated at higher temperature (130 °C), anatase to rutile transformation was avoided after calcination treatment as high as 800 °C. The highest photocatalytic activity was detected from the sample hydrothermally treated at 130 °C and calcined at 800 °C for which the highest degree of crystallinity and anatase phase as well as enhanced pore connectivity was obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.