Abstract
This study aims to synthesize and evaluate the properties of bio-sourced poly(1,3-propanediol) laurate (PO3G-LA) as a plasticizer in the fabrication of poly(1,3-propanediol) laurate/L-polylactic acid (PO3G-LA/PLLA) thin films. Utilizing an esterification reaction between poly(1,3-propanediol) (PO3G) and lauric acid (LA), PO3G-LA is synthesized and incorporated into PLLA films via solution casting. Results demonstrate that PO3G-LA exhibits excellent compatibility with PLLA, markedly enhancing the toughness and slightly improving the thermal stability of the resulting films. Specifically, the addition of 20% PO3G-LA increases the elongation at the break of the films to 190%, indicating enhanced flexibility. Accelerated degradation experiments conducted at 60 °C revealed that the presence of PO3G-LA under neutral conditions had minimal impact on the degradation rate of the film samples. Conversely, variations in the PO3G-LA content of the films when exposed to acidic and alkaline conditions were found to influence their degradation rates.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call