Abstract
A soluble low bandgap poly (pyrrole methine) with alkoxyl substituent, poly {(3-hexanoyl)pyrrole-[2,5-diyl(p-tetradecyloxybenzylidene)]} (PHPDTBE), was synthesized and characterized by 1H nuclear magnetic resonance (1H-NMR), Fourier transform-infrared (FT-IR), elemental analysis (EA) and gel permeation chromatography (GPC). PHPDTBE was readily soluble in weak polar organic solvents. The absorption peaks of PHPDTBE solution and film were located at around 458 and 484 nm, respectively. The optical bandgaps of PHPDTBE film for indirect allowed and direct allowed transitions were measured to be 1.66 and 2.35 eV, respectively. PHPDTBE film had few defects in the energy band and the Urbach energy of PHPDTBE film was calculated to be about 0.19 eV. The resonant third-order nonlinear optical susceptibilities of PHPDTBE solution and film measured by degenerate four-wave mixing (DFWM) technique at 532 nm were all in the order of 10–8 esu, which was about 1~3 orders of magnitude larger than that of the other ordinary π-conjugation polymers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.