The Al2-xCrxO3 powders with dopant contents ranging from x = 0.005 to 0.35 have been prepared by sol-gel method. The powders were prepared from aluminium nitrate Al(NO3)3·9H2O, chrome nitrate Cr(NO3)3·9H2O, and citric acid and heat-treated at 650-1300°C for 5 h. The effect of dopant concentration and heat-treating temperature on the structural and optical properties of the synthesized samples has been studied. The results showed that the structure, the size and optical properties of Al2-xCrxO3 crystallites strongly depended on the mole fraction x and heating temperature. At low heating temperatures, the samples with the low mole fraction x exhibit γ-Al2O3 phase and the emission spectra consist of a broad asymmetric peak with the maximum at 691 nm. With the high mole fraction x, the samples consist of α-Al2O3 and Cr2O3 phases. By increasing the mole fraction x, the emission bands are broadened and shifted towards the long-wavelength side. At high heating temperatures, all the synthesized samples are α-Al2O3 single phase and the emission spectra mainly consist of lines at 691.6 and 693.2 nm. [DOI: 10.1380/ejssnt.2011.531]
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.