Abstract
Niobium aluminide-based composites reinforced with in situ and externally added Al 2O 3 and TiC particulates were fabricated by hot-pressed sintering at 1400 °C. In particular, Nb 2Al–Al 2O 3–TiC in situ composites were successfully obtained from the raw powder mixtures of Nb60Al40 (in at.%)–TiO 220C8 (in wt.%) by means of this process. The influences of ceramic particulates on the microstructures, flexural strength and fracture toughness were examined. The experimental results indicate that the presence of ceramic particulates yielded a remarkable improvement in both the strength and fracture toughness in comparison with previous results for monolithic niobium aluminide compounds.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.