Abstract
Three kinds of polyamide-imide (PAI) were synthesized. The polyimide prepolymer was synthesized from 4,4'-diphenylmethane diisocyanate (MDI) and 3,3'-4,4'-benzophenone tetracarboxylic dianhydride (BTDA), after which the prepolymer was reacted respectively with terephthalic acid (TPA), isophthalic acid (IPA), and 4,4'-oxybisbenzonic acid (OBBA) to form PAI-1, PAI-2, and PAI-3. Their chemical structures were characterized using elemental analyses (EA), Fourier transform infrared spectrometry (FTIR), and nuclear magnetic resonance (NMR). The thermal properties, electrical properties, solubility, and mechanical properties of these PAIs, and the peel strength retention and electrical properties of PAI/Cu laminates were measured. The dielectric constants of PAI laminates were lower than 5.5 and the dissipation factors were lower than 0.035, and were in the order of PAI-3 < PAI-1 < PAI-2. These PAI/Cu laminates exhibited peel strength higher than 2.30 kN/m under normal circumstances and higher than 2.15 kN/m after heating. The order of peel strength was PAI-1 > PAI-3 > PAI-2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.