Abstract
Sr3Al2O6:Eu3+ red phosphor was synthesized by co-precipitation and investigated their crystal structures and luminescent properties in detail. EuCl3 was used as rare earth sources to replace Eu2O3, which saving cost significantly. X-ray diffraction(XRD) and scanning electron microscopy (SEM) result indicated that the as-prepared phosphors was calcined at 1150 oC for 2h crystalized in cubic phase with space group of Pa-3 and uniform morphology. The average diameter of the phosphors were 1.8um. Excitation spectrum and emission spectrum results shows when Boric acid was added 3wt% and Eu3+ was added x=0.04((Sr1-xEux)3Al2O6), the red emission of Eu3+ centers was shown at peak of 611nm under near ultraviolet excitation with wavelength of 393nm. The emission spectrum was line spectrum. Luminous intensity achieved the optimum. The thermal quenching experiments indicated that it had thermal stability in the temperature of 20 oC -80 oC.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.