Abstract
A series of Eu 2+-doped alkaline-earth apatites (alkaline-earth=Ca, Sr and Ba) were synthesized by a solid state reaction method with excess chlorides, and the effect of the used excess chlorides on the luminescent property of the synthesized products was discussed. Photoluminescence measurements showed that Eu 2+-doped calcium apatite exhibited intensely blue wide-band emission peaking at 457 nm under near UV excitation among the Eu 2+-doped Ca, Sr and Ba apatites. Blue and white LEDs were successfully fabricated by pre-coating the calcium apatite phosphors onto ∼395 nm-emitting InGaN chips. The CIE coordinates, color temperature, luminous efficacy and rendering index value of the fabricated white LED are (0.3432, 0.3234), 4969 K, 8 lm/W and 80, respectively. The results indicate that the Eu 2+-activated calcium apatite phosphor is a promising candidate as a blue component for fabrication of near UV-based white LEDs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.