Abstract
AbstractA series of amphiphilic graft copolymers consisting of poly(vinyl chloride) (PVC) main chains and poly(vinyl pyrrolidone) (PVP) side chains, i.e. PVC‐g‐PVP, was synthesized via atom transfer radical polymerization (ATRP), as confirmed by 1H NMR, FT‐IR spectroscopy, and gel permeation chromatography (GPC). Transmission electron microscope (TEM) and small angle X‐ray scattering (SAXS) analysis revealed the microphase‐separated structure of PVC‐g‐PVP and the domain spacing increased from 21.4 to 23.9 nm with increasing grafting degree. All the membranes exhibited completely amorphous structure and high Young's modulus and tensile strength, as revealed by wide angle X‐ray scattering (WAXS) and universal testing machine (UTM). Permeation experimental results using a CO2/N2 (50/50) mixture indicated that as an amount of PVP in a copolymer increased, CO2 permeability increased without the sacrifice of selectivity. For example, the CO2 permeability of PVC‐g‐PVP with 36 wt% of PVP at 35°C was about four times higher than that of the pristine PVC membrane. This improvement resulted from the increase of diffusivity due to the disruption of chain packing in PVC by the grafting of PVP, as confirmed by WAXS analysis. Copyright © 2011 John Wiley & Sons, Ltd.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.