Nickel hydroxide with a unique mixed phase α/β-Ni(OH)2 was prepared by partially substituting Ca2+ for Ni2+ with supersonic co-precipitating method firstly. The crystal structure and morphology of the samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). The results show that the Ca-substituted Ni(OH)2 by adding PO4 3− is α/β mixed phase, while the undoped Ni(OH)2 and the Ca-substituted Ni(OH)2 without adding PO4 3− are pure β phase. Furthermore, the Ca-substituted Ni(OH)2 by adding PO4 3− exhibits irregular shape and contains many intercalated water molecules and anions as proven by SEM and FT-IR. Meanwhile, the prepared samples were added into micro-sized beta nickel hydroxide to form biphase electrode materials for Ni-MH battery. The electrochemical performances of the biphase electrodes were characterized by cyclic voltammetry (CV) and charge/discharge tests. The results demonstrate that the biphase electrode with mixed phase α/β-Ni(OH)2 exhibits higher electrochemical activity, better electrochemical reversibility and charge efficient, higher discharge potential, and better cyclic stability. The specific discharge capacity of Ca-substituted α/β-Ni(OH)2 electrode can retain 271.7 and 238 mAh/g after 80 cycles at 0.2 and 0.5 C, respectively. This indicates that it may be a promising positive active material for alkaline secondary batteries. The results reported in this work may be useful for the designing and synthesizing of nickel hydroxide materials with superior performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.