Abstract
Fine powders of Ln 0.6Ca 0.4FeO 3−δ (Ln Pr, Nd, Sm) were prepared by a glycine-nitrate process (GNP). The preparation process, thermal properties, phase constituents, and microstructure of the samples were characterized by FT-IR, TG-DSC, XRD and TEM, respectively. The results show that all of the powders have perovskite-type structure with orthorhombic symmetry and mean particle size of 25 nm. The relative density of Pr 0.6Ca 0.4FeO 3−δ and Nd 0.6Ca 0.4FeO 3−δ decreased with sintering temperature, while increased for Sm 0.6Ca 0.4FeO 3−δ. The DC four-probe measurement indicated that both Pr 0.6Ca 0.4FeO 3−δ and Nd 0.6Ca 0.4FeO 3−δ exhibit fairly high electrical conductivity, over 100 S cm −1 at T > 650 °C, high enough for application as cathode materials for IT-SOFC. The temperature dependence of the conductivity for Nd 0.6Ca 0.4FeO 3−δ consists of two straight lines with activation energies of 160.2 and 18.6 kJ mol −1, respectively, for the sample sintered at 1100 °C for 2 h. The conduction mechanism of the materials is discussed in terms of non-stoichiometry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.