Abstract
Ultra-fine hafnium carbide powder was synthesized by the carbothermal reduction of HfO2 at 1600°C using the modified spark plasma sintering (SPS) apparatus. The synthesized powder had a fine particle size of about 125nm and a low oxygen content of below 0.5wt%. The purity of the powder was >99.9% excluding Zr, and 99.6% when including Zr impurity. The intermediate reactions and particle growth were minimized due to the low synthesis temperature, fast heating/cooling rate and the effect of current during the modified SPS process. A relatively large amount of HfC powder could be synthesized by the new synthesis method (>175g/day). HfC ceramics with high relative density (>96%) were obtained after sintering the synthesized powder without sintering additives at 2300°C for 30min under 100MPa pressure by SPS. The average grain size of the obtained specimen was about 6μm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.