Abstract
AbstractHigh molecular weight and regular molecular structure poly(propylene carbonate) (PPC) was successfully synthesized from carbon dioxide and propylene oxide. The PPC copolymer structure was an exact alternating copolymer as evidenced by the 13C‐NMR technique. Degradative behavior of the PPC was conducted by soil burial and buffer solution immersion (pH = 6) tests, respectively. The results showed that the weight loss of soil buried in PPC films increased more slowly than that immersed in the buffer solution after 6‐month exposure. However, the weight loss of sample immersed in the buffer solution increased rapidly during the first 2 months and reached a value of 4.59%. Water sorption measurement also revealed that the PPC membranes immersed in buffer solution were more hydrophilic than those in soil burial tests. The degradation mechanism of PPC membranes was correlated with the sample morphologies, FTIR, and 1H‐NMR spectra. The SEM morphologies were consistent with the weight loss and water sorption measurements. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 1840–1846, 2004
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.