Synthesis and crystal structure determination of yttrium ultraphosphate YP 5O 14

Abstract

The crystal structure of monoclinic YP 5O 14 (space group C2/ c, a=12.919(2) Å, b=12.796(4) Å, c=12.457(2) Å, β=91.30(1)°, Z=8) has been refined from single-crystal X-ray diffraction data. Full-matrix least-squares refinement on F 2 using 2249 independent reflections for 183 refinable parameters results in a final R value of 0.027 ( ωR=0.069). The structure is isotypic with HoP 5O 14. This structure is built up from infinite layers of PO 4 tetrahedra linked through isolated YO 8 polyhedra. The three-dimensional cohesion of the framework results from Y–O–P bridges. This crystal structure refinement leads to the calculated X-ray diffraction powder pattern of this monoclinic polymorph, which has been the starting point of a thorough study of the solid-state synthesis of this ultraphosphate. This investigation further leads to a better outstanding of features observed during the synthesis of powdered samples. The thermal behavior of this ultraphosphate has been studied by DTA and TGA analyses. The infrared and Raman spectroscopic characterizations have been carried out on polycrystalline samples. The luminescence properties of the Eu 3+ ion incorporated in the monoclinic C2/ c polymorph of YP 5O 14 as local structural probe show that in YP 5O 14: 5% Eu 3+ sample, the Eu 3+ ions are distributed over the two Y 3+ crystallographic sites of C 2 symmetry of this structure.