Abstract
ABSTRACTPure and Fe-doped In2O3 nanocrystalline powder was synthesized using a solution chemistry route based on the Sol-Gel process, which is a simple and inexpensive technique and produces long-time stable stock solutions. The X-ray diffraction patterns revealed the formation of nanocrystalline particle size with well-crystallized cubic bixbyte structure. The average crystal size was calculated from XRD patterns using Debye-Scherrer's equation for the (222) peak and found to be 8 nm. This observation agrees well with the particle size estimated from transmission electron microscopy (TEM). The observed Raman peaks in the doped materials are shifted towards the lower frequency up to 15 cm−1 and we did not observed any additional new Raman modes with Fe doping. This clearly indicates that Fe ions are indeed occupying interstitial/substitutional sites in the host In2O3, in agreement with XPS measurements. Magnetic properties were studied using superconducting quantum interface device magnetometer (Quantum design MPMS XL-7). Preliminary magnetic measurement results suggest the incorporation of the dopants in the diamagnetic In2O3-host structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.