Abstract
Waterborne polyurethane modified by acrylate/nano-ZnO (PUA/ZnO) was synthesized and used to improve the wet rubbing fastness of reactive dyed cotton fabric. The reaction conditions were optimized and the products were characterized by FT-IR, TG, DSC, SEM, and particle size distribution. The dyed cotton fabrics were finished with PUA/ZnO emulsion and the rubbing fastness, ultraviolet resistant property, and wearability of treated fabrics were measured. The wet rubbing fastness of treated fabrics was increased by about 0.5–1 rate to achieve 3–4 rate, and the ultraviolet protection factor (UPF) achieved 50+ level. The whiteness, air permeability, and elongation at break of treated fabric were not decreased significantly. SEM showed that the smooth and reticular coating on the surface of treated fabric reduced the mechanical friction force between dyed fabric and rubbing cloth, and thus improved the rubbing fastness. The decomposition temperature of finished fabric was increased by 50–80 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.