Abstract
Photocurable polymers with high transparency and thermal stability were synthesized by reaction between a commercial epoxy resin (NC9110) containing cyclohexane moiety and various kinds of cinnamic acids such as trans-cinnamic acid (CA), 3-hydroxy-trans-cinnamic acid (HCA) and 4-methoxy-trans-cinnamic acid (MCA). The photocurable polymers were synthesized with equal equivalent weight ratio of epoxy and cinnamate group. The chemical structures of the synthesized polymers were confirmed by 1H-NMR and FT-IR spectroscopies. Optical transmittance and thermal stability of the photocured polymers were investigated using UV-Visible spectroscopy and thermogravimetric analysis (TGA), respectively. It was confirmed that the polymers could form thin films with very smooth surface and could be efficiently cured by UV irradiation. It was also found that the polymer after curing showed a good thermal stability and optical transmittance. There was no significant transmittance change after heat treatment at 250 degrees C for 1 h and showed no noticeable weight loss up to 360 degrees C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.