Abstract
The title compounds were synthesized by a hydrothermal route from a 1:1 molar ratio of lithium fluoride and transition-metal acetate in an excess of water. The crystal structures were determined using a combination of powder and/or single-crystal X-ray and neutron powder diffraction (NPD) measurements. The magnetic structure and properties of Co(OH)F were characterized by magnetic susceptibility and low-temperature NPD measurements. M(OH)F (M = Fe and Co) crystallizes with structures related to diaspore-type α-AlOOH, with the Pnma space group, Z = 4, a = 10.471(3) Å, b = 3.2059(10) Å, and c = 4.6977(14) Å and a = 10.2753(3) Å, b = 3.11813(7) Å, and c = 4.68437(14) Å for the iron and cobalt phases, respectively. The structures consist of double chains of edge-sharing M(F,O)6 octahedra running along the b axis. These infinite chains share corners and give rise to channels. The protons are located in the channels and form O-H···F bent hydrogen bonds. The magnetic susceptibility indicates an antiferromagnetic ordering at ∼40 K, and the NPD measurements at 3 K show that the ferromagnetic rutile-type chains with spins parallel to the short b axis are antiferromagnetically coupled to each other, similarly to the magnetic structure of goethite α-FeOOH.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.