Abstract
A convenient and effective technique for polymerization to produce the poly(acrylic acid-co-acrylamide)/montmorillonite superabsorbent composite in aqueous solution was developed, in which the reaction was initiated by the glow discharge electrolysis (GDE) plasma rather than chemical initiators. The resulted superabsorbent has higher water absorbency, for example, 1024 g g −1 for distilled water and 56 g g −1 for 0.9% NaCl solution. To optimize the synthesis conditions, the following parameters were examined in detail: the discharge voltage, discharge time, ratio of acrylic acid to acrylamide, neutralization of acrylic acid, amount of crosslinking agent and montmorillonite added. The superabsorbent composite was characterized by Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). Results indicated that montmorillonite was effectively bonded with polymer. Moreover, the water absorbency, water retention and thermal stability of the superabsorbent composite prepared by GDE were higher than those of the superabsorbent composite by conventional chemical method under the same polymerization conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.