Synthesis and Characterization of Single-Phase α-Cordierite Glass-Ceramics for LTCC Substrates from Tuff.

Abstract

Single-phase α-cordierite glass-ceramics for a low-temperature co-fired ceramic (LTCC) substrate were fabricated from tuff as the main raw material, using the non-stoichiometric formula of α-cordierite with excess MgO without adding any sintering additives. The sintering/crystallization behavior and the various performances of dielectric properties, thermal expansion, and flexural strength of the glass-ceramics were detected. The results indicated that only single-phase α-cordierite crystal was precipitated from the basic glass sintered at the range 875-950 °C, and μ-cordierite crystal was not observed during the whole sintering-crystallization process. The properties of glass-ceramics were first improved and then deteriorated with the increase in tuff content and sintering temperature. Fortunately, the glass-ceramics sintered at 900 °C with 45 wt.% tuff content possessed excellent properties: high densify (2.62 g∙cm-3), applicable flexural strength (136 MPa), low dielectric loss (0.010, at 10 MHz), low dielectric constant (5.12, at 10 MHz, close to α-cordierite), and suitable coefficients of thermal expansion (CTE, 3.89 × 10-6 K-1).