Synthesis and characterization of pure strontium apatite particles and nanoporous scaffold prepared by dextrose-templated method

Abstract

Strontium shows an increasing interest on bone formation and bone resorption prevention. Here, pure apatite strontium (Ap-SrOH) [Sr5(PO4)3(OH), strontium hydroxyapatite] particles were prepared by the precipitation method using Sr(NO3)2 · 6H2O and (NH4)2HPO4 as reagents. Scanning electron microscope, transmission electron microscope combined with electron diffraction, X-ray diffraction, Fourier transform infrared spectra (FTIR), variable temperature FTIR and thermo gravimetric analysis were employed to evaluate the crystalline structure, chemical composition, and thermal stability of the Ap-SrOH particles. The results show that phase pure Ap-SrOH particles were prepared by wet precipitation. The obtained Ap-SrOH particles are single crystal in phase structure, they have hexagonal fusiform shape, and their size is about 30–180 nm in diameter, and 0.4–2.5 μm in length. The cell MTT assay evaluations indicate that Ap-SrOH particles have very low cytotoxicity. Furthermore, nanoporous Ap-SrOH scaffolds were synthesized by anhydrous dextrose template method. After mixed 5–10 wt% of anhydrous dextrose with Ap-SrOH particles, pressed into discs, and sintered in microwave muffle furnace at 600 °C, the scaffolds with both nanoporous and nanotopography were formed. Cell culture of MC3T3-E1 osteoblasts in vitro show cells grow well on nanoporous Ap-SrOH scaffold. Therefore, Ap-SrOH particles and their nanoporous scaffolds are promising biomaterials for bone repairing and bone disease (e.g. osteoporosis) healing.