Abstract
In this research our aim was to obtain pure and Zn doped lead hydroxide nanostructure by chemical root method. For making reaction solution we used 0.04M aqueous solution of lead nitrate and zinc chloride was mixed with 0.08M aqueous solution of sodium hydroxide 0.001M aqueous solution of TEA (Tri Ethanol Amine) was also added to reaction solution. Powder was annealed at 190°C. The prepared pure and Zn doped lead oxide nanostructure was characterized, X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution-transmission electron microscopy (TEM) and photo luminescence of the sample. The prepared pure and doped lead hydroxide consists of the average crystallites about 20 and 12nm and band gap obtained 4.93 and 5.25eV respectively. The pure lead oxide phosphor material shows a broad peak at 501nm (near to Green region) and Zn doped lead oxide show the peak at lower wavelength side 402nm (blue region).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call