Abstract
Yellow inorganic pigments PrxZr1-xSiO4 (x = 0–0.08) have been prepared by a novel non-hydrolytic sol-gel (NHSG) method at 750 °C for 2 h. Replacing Pr4+ for Zr4+ in ZrSiO4 increased the cell volume and changed the color from white to yellow gradually. The Si―O―Zr and Si―O―Pr bands were observed in the FT-IR spectra of xerogel, indicating it could reach homogeneous mixing at the atomic level. Therefore, it promoted the solid solution reaction between Pr and zircon at low temperature. The samples exhibit high doping limitation (x = 0.08) and brilliant yellow hue (b* = 69.48) in contrast with the previously reported praseodymium zircon yellow pigments. The intense of yellow hue was increased with increasing the Pr doping content due to the increase of Pr4+/Pr3+ species. After applying on bisque ceramic tiles, the pigment exhibited excellent coloration, high thermal stability and low solubility in molten glazes, indicating its potential application in ceramic decoration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.