Synthesis and characterization of proton‐conducting copolyimides bearing pendant sulfonic acid groups

Abstract

AbstractA series of sulfonated copolyimides (co‐SPIs) bearing pendant sulfonic acid groups were synthesized from 1,4,5,8‐naphthalenetetracarboxylic dianhydride (NTDA), bis(3‐sulfopropoxy) benzidines (BSPBs), and common nonsulfonated diamines via statistical or sequenced polycondensation reactions. Membranes were prepared by casting their m‐cresol solutions. The co‐SPI membrane had a microphase‐separated structure composed of hydrophilic and hydrophobic domains, but the connecting behavior of hydrophilic domains was different from that of the homo‐SPIs. The co‐SPI membranes displayed clear anisotropic membrane swelling in water with negligibly small dimensional changes in the plane direction of the membrane. With water uptake values of 39–94 wt %, they showed dimensional changes in membrane thickness of about 0.11–0.58, which were much lower than those of homo‐SPIs. The proton conductivity σ values of co‐SPI membranes with ion exchange capacity values ranging from 1.95–2.32 meq/g increased sigmoidally with increasing relative humidity. They displayed σ values of 0.05–0.16 S/cm at 50 °C in liquid water. Increasing temperature up to 120 °C resulted in further increase in proton conductivity. The co‐SPI membranes showed relatively good conductivity stability during the aging treatment in water at 100 °C for 300 h. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 1545–1553, 2005