Abstract
P(AN-co-VAc)/Fe2O3 core-shell nanocapsules were synthesized by miniemulsion polymerization and P(AN-co-VAc)/Fe2O3@PEDOT core-shell structure was constituted by oxidative polymerization. Homogeneous nanofibers were obtained from the core-shell nanocapsules. Characterizations were performed by XRD, GPC, UV-vis, and FTIR-ATR. SEM, AFM, and TEM. Molecular weight and Tg of the nanocapsules were effected by the increase in γ-Fe2O3 NPs. Nanofiber resistance (Rnfb) drastically decreased from 2700 to 110 kΩ.cm2 by the inclusion of γ-Fe2O3 NPs into the nanocapsules 8.3 kΩ.cm2 obtained after coating with PEDOT. The electrochemical Impedance results were fitted to models of [R (Q(R (CR)))] and [R (Q(R (QR)))], respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Polymeric Materials and Polymeric Biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.