Abstract
Multiblock copolymers based on poly(arylene ether sulfone) and polybenzimidazole (PBI) with different block lengths were synthesized by coupling carboxyl functional aromatic poly(arylene ethers) with ortho diamino functional PBI oligomers in NMP, selectively doped with phosphoric acid, and evaluated as a high temperature proton exchange membrane (PEM). Transparent and ductile membranes were produced by solvent casting from DMAc. From dynamic mechanical analysis (DMA), the neat copolymer membranes showed two distinct glass transition temperatures which implies the existence of a nanostructured morphology in the membranes. These two nanophases became more distinct with increasing block length. The membranes were immersed in various concentrations of phosphoric acid solution to produce the proton conductivity. The doping level increased with increasing concentration of the acid solution and a maximum doping level of 12 was achieved when 14.6M phosphoric acid solution was used. The acid doped membranes showed significantly reduced swelling behavior compared to a control conventional phosphoric acid doped PBI homopolymer system which appears to be related to the selective sorption into the PBI phase. The ionic conductivity of the doped samples at 200°C afforded up to 47mS/cm without external humidification. The protonic conductivity was found to increase with block length at a given doping level, reflecting the sharpness of the nanophase separation and the effect was even more prominent at a low doping level of 6–7. It is suggested that the phosphoric acid doped multiblock copolymer system would be a strong candidate for high temperature and low relative humidity PEM applications such as those required for stationary power.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.