Abstract
Ultrafine TiO 2 dispersed nickel composite coatings have been prepared by direct current deposition process on steel substrate from Watt's bath to improve the surface mechanical property of conventional nickel coating. To resist agglomeration of ultra fine particles in plating bath due to high surface free energy and to get homogeneous coating, magnetic stirring was applied during deposition with prior ultrasonic agitation. For de-agglomeration, Hexa decylpyridinium bromide (HPB) was used in varying quantity in plating bath as surfactant. Characterization of TiO 2 powder as well as microstructure, hardness and wear properties of the coatings were studied by means of XRD, SEM, microhardness tester and ball-on-plate type wear tester. TiO 2 incorporation in the coatings was uniform and dispersion of TiO 2 was below 100 nm size along with the faceted nickel matrix. Selective amount of HPB addition produces hard orientation of nickel in the composite coating along with better TiO 2 co-deposition rate leading to higher microhardness and wear resistance. Wear is mainly adhesive in nature and the worn out TiO 2 particles shift it nominally to abrasive mechanism.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.