Synthesis and characterization of new aromatic polyesters containing pendent naphthyl units

Abstract

AbstractTwo bisphenols, viz., 4,4′‐[1‐(2‐naphthalenyl)ethylidene]bisphenol and 4,4′‐[1‐(2‐naphthalenyl) ethylidene]bis‐3‐methylphenol were prepared by condensation of commercially available 2‐acetonaphthanone with phenol and o‐cresol, respectively. A series of new aromatic polyesters containing pendent naphthyl units was synthesized by phase‐transfer‐catalyzed interfacial polycondensation of these bisphenols with isophthaloyl chloride, terephthaloyl chloride, and a mixture of isophthaloyl chloride/terephthaloyl chloride (50 : 50 mol %). Inherent viscosities of polyesters were in the range 0.83–1.76 dL g−1, while number average molecular weights (Mn) were in the range 61,000–235,000 g mol−1. Polyesters were readily soluble in organic solvents such as dichloromethane, chloroform, tetrahydrofuran, m‐cresol, pyridine, N,N‐dimethylformamide, N,N‐dimethylacetamide, and 1‐methyl‐2‐pyrrolidinone at room temperature. Tough, transparent, and flexible films were cast from a solution of polyesters in chloroform. X‐Ray diffraction measurements displayed a broad halo at 2θ ≅ 19° indicating the amorphous nature of polyesters. Glass transition temperatures of polyesters were in the range 209–259°C. The temperature at 10% weight loss (T10), determined by TGA in nitrogen atmosphere, of polyesters was in the range 435–500°C indicating their good thermal stability. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010