Synthesis and characterization of multi‐block copolymers containing poly [(3‐hydroxybutyrate)‐co‐(3‐hydroxyvalerate)] and poly(ethylene glycol)

Abstract

AbstractVarious problems, including high crystallinity, high melting temperature, poor thermal stability, hydrophobicity and brittleness, have impeded many practical applications of poly[(3‐hydroxybutyrate)‐co‐(3‐hydroxyvalerate)] (PHBV) as an environmentally friendly material and biomedical material. In the work reported here, multi‐block copolymers containing PHBV and poly(ethylene glycol) (PHBV‐b‐PEG) were synthesized with telechelic hydroxylated PHBV as a hard and hydrophobic segment, PEG as a soft and hydrophilic segment and 1,6‐hexamethylene diisocyanate as a coupling reagent to solve the problems mentioned above. PHBV and PEG blocks in PHBV‐b‐PEG formed separate crystalline phases with lower crystallinity levels and lower melting temperatures than those of phases formed in the precursors. The crystallite dimensions of the two blocks in PHBV‐b‐PEG were smaller than those of the corresponding precursors. Compared to values for the original PHBV, the maximum decomposition temperature of the PHBV block in PHBV‐b‐PEG was 16.0 °C higher and the water contact angle was 9° lower. In addition, the elongation at break was 2.8% for a pure PHBV fiber but 20.9% for a PHBV/PHBV‐b‐PEG fiber with a PHBV‐b‐PEG content of 30%. PHBV‐b‐PEGs can overcome some of the disadvantages of pure PHBV; it is possible that PHBV might be a good candidate for the formulation of environmentally friendly materials and biomedical materials. Copyright © 2010 Society of Chemical Industry