Abstract
Magnetite nanoparticles were prepared by partial oxidation of Fe(II) ions of an aqueous suspension of hydroxysulfate green rust which was obtained by precipitation of Fe(II) ions. This magnetite was mixed with zeolite synthesized from coal fly ash to obtain the magnetic adsorbent and the final product characterization was made. By analysis of scanning electron microscopy and X-ray diffraction, images of clusters of magnetite nanoparticles were observed and crystallite sizes of 17 nm were determined, respectively. In thermal analysis, the weight ratio of 1:3 for magnetite-zeolite in the magnetic adsorbent was measured and a non-magnetic product at 974 °C was found in both magnetite and magnetic adsorbent. Magnetization measurements described small hysteresis from the clusters of magnetite nanoparticles. Fourier Transform Infrared spectroscopy analysis indicated that the synthesized zeolite is a hydroxy sodalite and evidences of formation of the magnetic adsorbent were observed. The performance of magnetic separation technique was evaluated and it was comparable to the centrifugation process. The magnetic adsorbent indicated a potential application for adsorption of dye Reactive Orange 16 from aqueous solution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.