Abstract
Magnetic iron oxide (Fe3O4 and γ-Fe2O3) and iron carbide (Fe3C) nanoparticles of different geometrical shapes: cubes, spheres, rods and plates, have been prepared by thermal decomposition of a mixture containing the metal precursor Fe(CO)5 and the stabilizer polyvinylpyrrolidone (PVP) at 300°C in a sealed cell under inert atmosphere. The thermal decomposition process was performed for 4 or 24h at ([PVP]/[Fe(CO)5]) (w/v) ratio of 1:1 or 1:5. Elemental iron nanospheres embedded within a mixture of amorphous and graphitic carbon coating were obtained by hydrogen reduction of the prepared iron oxide and iron carbide nanoparticles at 450°C. The formation of the graphitic carbon phase at such a low temperature is unique and probably obtained by catalysis of the elemental iron nanoparticles. Changing the annealing time period and the ([PVP]/[Fe(CO)5]) ratio allowed control of the composition, size, size distribution, crystallinity, geometrical shape and magnetic properties of the different magnetic nanoparticles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.