Abstract
Aqueous polyurethane emulsion was prepared with diphenylmethane diisocyanate (MDI), polybutylene adipate diol (PBA-1000) as main raw materials and 2, 2-dihydroxymethyl propionic acid (DMPA) as hydrophilic chain extender. On this basis, epoxy resin E-44 was introduced to modify the polyurethane prepolymer, and epoxy resin modified waterborne polyurethane emulsion was obtained. In order to obtain better performance waterborne polyurethane, the effect of DMPA content、the amount of epoxy resin added and modification method on the properties of polyurethane was discussed. The results show that when the DMPA content is 4wt%, the overall performance of the emulsion and the film is the best. And the addition of epoxy resin significantly improves the water resistance, solvent resistance and tensile strength of the waterborne polyurethane film, and its hardness and thermal stability are also improved to a certain extent. When the amount of epoxy resin added is 8wt%, the storage stability decreases significantly, the suitable amount of epoxy resin added is 6wt%. The overall performance of the film obtained by chemical modification is better than that of physical modification.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.