Synthesis and characterization of electrical conducting nanoporous carbon structures

Abstract

Nanoporous organic xerogel compounds were prepared by sol–gel method from pyrogallol-formaldehyde (PF) mixtures in water using perchloric acid as catalyst. The preparation conditions of electrical conducting carbon (ECC) structures were explored by changing the pyrolysis temperature. The effect of this preparation parameters on the structural and electrical properties of the obtained ECCs were studied, respectively, by thermogravimetric analysis (TGA), nitrogen adsorption isotherms, IR spectroscopy and electrical conductivity measurements. The analysis of the obtained results revealed that, the polymeric insulating phase was transformed progressively with pyrolysis temperature into carbon conducting phase; this means the formation of long continuous conducting path for charge carriers when the carbon microparticles inside the structure agglomerated with thermal treatment and the samples exhibited tangible percolation behaviour where the percolation threshold can be determined by pyrolysis temperature. The temperature-dependent conductivity and the I( V) characteristics of the obtained ECC structures show a non-ohmic behaviour. The results obtained from TGA and differential thermal analyser (DTA) thermograms, scanning electron microscope (SEM) and transmission electron microscope (TEM) micrographs, IR spectroscopy and X-ray diffraction revealed that, the obtained ECC structures consist of amorphous and nanoporous electrical conducting carbon materials.