Abstract
The current research is focused on the chemical process and characterization of Co-based Y-type hexaferrite, electrochemically active polypyrrole doped with dodecylbenzene sulphonicacid (PPy-DBSA) and their composites. The microemulsion technique was used to produce hexaferrite with the formula Sr2Co2Fe12O22. The resistivity of pure ferrite specimens was 103 ohm-cm, which was lower than the 106 ohm-cm resistivity of the monomer utilized in the polymerization operation. As the temperature increases, the DC resistance decreases, revealing the specimens’ semiconductor nature. The cole-cole plots have been used to assess whether significant grain boundaries were involved in the dielectric relaxation process. By increasing the frequency, the electrochemical performance of all specimens was enhanced. Using the rate equation, ionic conductivity demonstrates that polarons are responsible for conduction. Because of the characteristics of the polymer PPY-conducting DBSA, the composites PPY/DBSA + Sr2Co2Fe12O22 exhibit a higher dielectric loss of 35 at 1 MHz. This specimen is perfect for electrical radiation shielding (EMI).These ferrites are widely used as permanent magnets, in microwave devices, high-density perpendicular media, and rigid disk media without lubricant and protective layers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.