Abstract
Background: To enhance the super capacitive properties of nanocomposites, the effective method is to combine carbon nanospheres with mesoporous structures with Gd3+:α-Sb2O4 inorganic nanocomposites (NC) to form hybrid electrodes. An as-prepared hybrid electrode material possesses increased energy density, high rate of reversibility and cyclic stability when incorporated in electrochemical cyclic voltammetric studies. Methods: In the present investigation, various wt % of C-nanospheres (Cx) (5 %, 10% and 20%) were decorated over Gd3+: α-Sb2O4 nanocomposites and were synthesized by coprecipitation method. XRD, SEM, EDX, UV-visible, and XPS are only a few of the analytical techniques used to describe the as-prepared hybrid nanocomposites. Electrochemical cyclic voltammetry was carried out in a 6 M KOH solution, three-electrode system. Results: The crystal structure and morphology of Cx: Gd3+@ α-Sb2O4 NC showed a mixed hexagonal phase and agglomerated tiny irregularly shaped morphology that appeared as the Cx concentration increased. Redshift in optical absorption peak appeared (near UV-edge), and the optical band gap (Eg) value increased from 3.53 eV to 3.65 eV. The electrochemical supercapacitor showed the highest specific capacitance of 989 F/g at the current density of 1 A/g for C20%:Gd3+@α-Sb2O4 NC compared with Cx:Gd3+@α-Sb2O4 (x = 5% and 10%) and undoped Gd3+:α-Sb2O4 NC. The change in phase angle and Rs value of 1.98 was attributed to the ideal supercapacitor properties. The cyclic stability after 5000 cycles with 79.71% capacitive retention was exhibited by C20%:Gd3+@α-Sb2O4 NC. Conclusion: The present research introduces ease of synthesis of hybrid electrode materials possessing high active surface area, increased energy density, high cyclic stability, and reversibility in an aqueous solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.