Abstract
<p>The purpose of this study was to produced bioplastic from chitosan-ganyong starch and compare its quality to commercial biodegradable plastic. This research was carried out by experimental method in laboratory. Making bioplastic film was done by dissolving, blending, printing, drying, and neutralizing process. Characterization of bioplastic film was performed by tensile strength test,% elongation, thickness, swelling, solubility, biodegradability and functional group analysis with FTIR. The produced bioplastic characterizations were compared to commercial biodegradable plastics. The results concluded that the qualities of bioplastic chitosan-ganyong starch are higher than commercial biodegradable plastics on tensile strength parameter (53,9644 Mpa : 18,4109 MPa),% elongation (1,8066 % : 3,7025%), and degradation ability (5 days : 30 days); but lower in thickness parameters (0.0350 mm: 0.0140 mm), % swelling (0.275%: 0.010%), and solubility (0.10%: 0.05%).</p><p><strong> </strong></p><p> </p>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have