Abstract
The synthesis and characterization of a MgNi alloy having La and Ce as catalysts, have been performed. The alloy behavior was studied at given fixed temperature and pressure during hydrogen absorption/desorption tests. The La and Ce addition was carried out starting from a commercial alloy, named “Firesteel”. The alloy synthesized has the following formula Mg68Ni26M5X, where X represents Si and Fe impurities and M stands for the mixture of rare earths metals. The alloy has been prepared by a melting process in an induction furnace equipped with a centrifugal casting system and then grinded, by both hydraulic press and ball milling. The alloy has been characterized by SEM, BET, XRD, DSC-TGA analysis and by a mass flow measurement apparatus. The experiments on alloy sample showed that, after activation, hydrogenation occurs at 300 °C in three stages at three different pressures: 3, 4 and 7 atm, involving respectively 0.15 wt%, 0.4 wt% and 2.2 wt% of hydrogen absorbed. Reversible hydride dehydrogenation, inside the mass flow measurement apparatus, requires a working temperature of 350 °C to obtain, with remarkable reaction rate, about 2.7%, hydrogen desorption.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.