Abstract
PurposeThe purpose of this paper is to conduct the directed synthesis of blue-colour aluminate spinel pigments based on spent aluminium–cobalt–molybdenum (ACM) catalyst and to study peculiar features of mineral formation processes and changes in their colour indices depending on composition and firing temperature.Design/methodology/approachAluminate spinel ceramic pigments with specified colour indices were synthesised by directed formation of their mineral composition and identification of the most rational technological parameters of production. Mineral composition of synthesised pigments was evaluated by X-ray phase analysis. The colour indices of pigments and pigment-containing glaze coatings were studied on the comparator colour. The chemical resistance of pigments was determined by loss of their weight loss after boiling in 1 N hydrochloric acid solution and 1 N sodium hydroxide solution.FindingsPeculiar features of formation of the mineral composition of aluminate spinel pigments based on the ACM catalyst were studied. The expediency of using magnesium and zinc oxides in their composition has been proved. It is found that for the formation of stable pigments of intense blue colour, a concentration of cobalt (II) oxide in the amount of 0.5 mol is sufficient, which is 23.1 Wt.%. The colour of such pigments is determined by the ratios of cobalt, magnesium and zinc aluminates, which form a spinel solid solution.Practical implicationsThe use of developed aluminate spinel pigments provides obtaining of high-quality glass coatings of blue colour, in particular, for ceramics.Originality/valueAluminium oxide in the spent ACM catalyst is predominantly in the active form (of amorphous aluminium hydroxide and y-Al2O3). This is a prerequisite for the use of this waste material as a complete substitute for chemically pure Al2O3 in the technology of aluminate spinel pigments and reduction of their firing temperature. Besides, spent ACM catalyst already contains 5 Wt.% of expensive cobalt (II) oxide in the form of stable colour-bearing phase CoAl2O4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.