ZSM–5/SBA–15 composite materials were successfully synthesised by a hydrothermal treatment method including three steps: 1) microporous phase seed formation (seed 1); 2) precursor addition (seed 2); 3) formation of the ZSM–5/SBA–15 composite material. The obtained samples were characterised by XRD, SEM, TEM, TPD–NH3, 27Al MAS NMR, 1H MAS NMR, and N2adsorption/desorption. It could be shown that the formation of both micro– and mesopores strongly depends on the duration and temperature of the above–mentioned crystallisation steps. The results obtained from XRD, SEM, TEM, and N2 adsorption/desorption indicated that the ZSM–5/SBA–15 composite materials have both microporous and mesoporous properties. The composite nature of the samples was demonstrated by SEM and TEM studies. The high acid sites number and strength of the ZSM–5/SBA–15 composite materials were shown using 27Al MAS NMR, 1H MAS NMR, and TPD–NH3 methods.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.