Synthesis and Application of Titanium Carbide (Ti3C2)-Cobalt Sulfide (Co3S4) Nanocomposites in Amino Acid Biosensing.

Abstract

Background The fabrication of titanium carbide (Ti3C2)-cobalt sulfide (Co3S4)-based biosensors with high sensitivity and selectivity can change the biosensor manufacturing industry completely. Molecular and clinical diagnostics, disease progression monitoring, and drug discovery could utilize these sensors for early biomarker detection. MXene (Ti3C2) is a two-dimensional material with exceptional electrical conductivity, hydrophilicity, great thermal stability, large interlayer spacing, and a high surface area. Ti3C2'sremarkable characteristics make it well-suited for biomolecule immobilization and target analyte detection. Co3S4is a transition metal chalcogenide that has shown great potential in biosensors. Co3S4 nanoparticles (NPs) can potentially enhance Ti3C2 electrocatalytic activity, particularly in amino acid detection. L-arginine is a semi-essential amino acid, and the body frequently uses it to support healthy circulation and plays a crucial role in protein synthesis. We fabricated the Ti3C2-Co3S4 biosensor for L-arginine detection. Aim This study aims to synthesize and apply Ti3C2-Co3S4 nanocomposites in amino acid biosensing. Materials and methods The Ti3C2 nanosheets were synthesized by the selective removal of an aluminum (Al) layer from the precursor (Ti3AlC2) using hydrofluoric acid (HF). The resulting mixture serves as an etchant, especially targeting the Al layers on Ti3AlC2while protecting the desired MXene layers at room temperature. Cobalt nitrate hexahydrate was dissolved in deionized water. Sodium hydroxide was added to the cobalt solution and stirred. Thioacetamide was added to the above solution and stirred (Solution B). A mixture of Solution A and Solution B was stirred for 30 minutes. The mixture is transferred to a hydrothermal reactor and maintained at a temperature of 180°C for 12 hours. Once the reaction completes, we cool the resultant mixture to room temperature and then filter it using the washing technique. The sample underwent a 12-hour drying process at 80°C. Results This study investigated the use of a biosensor that employed Ti3C2-Co3S4 NPs to detect the concentration of L-arginine. The X-ray diffraction (XRD) shows clear and distinct peaks, which means that the synthesized Ti3C2-Co3S4 nanostructures have a crystalline structure.Scanning electron microscopy (SEM) analysis revealed that the sheetlike structure of synthesized Ti3C2-Co3S4 nanostructuresrevealedthe crystalline morphology. The results of this study show that the Ti3C2-Co3S4NP-based biosensor can be used to detect L-arginine in a sensitive and selective way. Conclusion This study investigated the synthesis of Ti3C2-Co3S4NPs and their ability to detect L-arginine levels and show a distinct correlation between the L-arginine concentration and the fluorescence intensity, demonstrating the biosensor's effectiveness in detecting L-arginine levels.