Syntheses and Characterization of 4-Octyloxybenzyl Substituted Diketopyrrolopyrrole-based Red Emitting Copolymers with Low Turn-on Voltage

Abstract

Two novel diketopyrrolopyrrole-based alternating copolymers, poly(2,7-(9,9-diethyl)-fluorenylvinylene-alt-2,5-bis(4′-octyloxyphe- nylmethyl)-3,6-bis(4-vinylenephenyl)pyrrolo[3,4-c]pyrrole-1,4-dione) (P1) and poly(1,4-(2,5-dioctyl- oxy)-phenylenevinylene-alt-2,5-bis(4′-octyloxyphenylmethyl)-3,6-bis(4-vinylenephenyl)pyrrolo[3,4-c]pyrrole-1,4-dione) (P2) were synthesized through Wittig polycondensation in good yields. P1 and P2 were characterized by NMR, FT-IR, UV-Vis, photoluminescence (PL) and electroluminescence (EL). EL devices with ITO/PEDOT/polymer/CsF/Al exhibited red-emitting light with the maximum EL wavelength at 620 nm and 682 nm. The results show that PL quantum yield of the polymers in thin film can be improved through N-alkylation of diketopyrrolopyrrole (DPP) with bulky substituent. EL performance of P2 was better than P1, which might be due to 1,4-dioctyloxybenzene of P2 enhancing the hole-transporting to make more charge balance. EL devices of P1 and P2 possessed low turn on voltage (2.4 V and 2.1 V, respectively), which was an advantage for PLED.