Abstract
AbstractNarrow‐bandgap mixed Pb‐Sn perovskite solar cells (PSCs) have great feasibility for constructing efficient all‐perovskite tandem solar cells, in combination with wide‐bandgap lead halide PSCs. However, the power conversion efficiency of mixed Pb‐Sn PSCs still lags behind lead‐based counterparts. Here, additive engineering using ionic imidazolium tetrafluoroborate (IMBF4) is proposed, where the imidazolium (IM) cation and tetrafluoroborate (BF4) anion efficiently passivate defects at grain boundaries and improve crystallinity, simultaneously relaxing lattice strain, respectively. Defect passivation is achieved by the chemical interaction between the IM cation and the positively charged under‐coordinated Pb2+ or Sn2+ ions, and lattice strain relaxation is realized by lattice expansion with the intercalation of BF4 anions into the perovskite lattice. As a result, the synergistic effects of the cation and anion in the IMBF4 additive greatly enhance the optoelectronic performance of half‐mixed Pb‐Sn perovskites, leading to much longer carrier lifetimes. The best‐performing half‐mixed Pb‐Sn PSC shows an efficiency above 19% with negligible hysteresis, while retaining over 90% of its initial efficiency after 1000 h in a nitrogen‐filled glovebox and showing a lifetime to 80% degradation of 53.5 h under continuous illumination.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.